Polymaker™ PC-ABS is a PC/ABS polymer blend which offers excellent toughness and heat resistance while displaying good surface finish and good compatibility with metal plating.
| Property | Test Method | Value |
|---|---|---|
| Density | ISO 1183, GB/T 1033 | 1.1 g/cm3 at 23°C |
| Melt index | 260°C, 5 kg | 11-17 g/10min |
| Light transmission | N/A | N/A |
| Flame retardancy | N/A | N/A |
| Effect of weak acids | N/A | Not resistant |
| Effect of strong acids | N/A | Not resistant |
| Effect of weak alkalis | N/A | Slight resistant |
| Effect of strong alkalis | N/A | Not resistant |
| Effect of organic solvent | N/A | Not resistant |
| Effect of oils and grease | N/A | No data available |
| Equilibrium water absorption | N/A | 0.352% |
| Property | Test Method | Value |
|---|---|---|
| Glass transition temperature | DSC, 10°C/min | 109 °C |
| Melting temperature | DSC, 10°C/min | N/A |
| Crystallization temperature | DSC, 10°C/min | N/A |
| Decomposition temperature | TGA, 20°C/min | N/A |
| Vicat softening temperature | ISO 306, GB/T 1633 | 135 °C |
| Heat deflection temperature (1.8MPa) | ISO 75 | 106.4 °C |
| Heat deflection temperature (0.45MPa) | ISO 75 | 111.7 °C |
| Thermal conductivity | N/A | N/A |
| Heat shrinkage rate | N/A | N/A |
| Property | Test Method | Value |
|---|---|---|
| Young’s modulus (X-Y) | ISO 527, GB/T 1040 | 1835 ± 65 MPa |
| Young’s modulus (Z) | N/A | 1677 ± 94 MPa |
| Tensile strength (X-Y) | ISO 527, GB/T 1040 | 39.9 ± 1.0 MPa |
| Tensile strength (Z) | N/A | 22.9 ± 1.2 MPa |
| Elongation at break (X-Y) | ISO 527, GB/T 1040 | 4.2 ± 0.3% |
| Elongation at break (Z) | N/A | 1.5 ± 0.1% |
| Bending modulus (X-Y) | ISO 178, GB/T 9341 | 2081 ± 106 MPa |
| Bending modulus (Z) | N/A | N/A |
| Bending strength (X-Y) | ISO 178, GB/T 9341 | 66.3 ± 0.9 MPa |
| Bending strength (Z) | N/A | N/A |
| Charpy impact strength (X-Y) | ISO 179, GB/T 1043 | 25.8 ± 1.3 kJ/m2 |
| Charpy impact strength (Z) | N/A | N/A |
| Low temperature impact strength (X-Y) | ISO 179-1/1eA:2010, -30°C | 13 ± 2 kJ/m2 |
| Low temperature impact strength (Z) | ISO 179-1/1eA:2010, -30°C | 1.5 ± 0.2 kJ/m2 |
| Parameter | Value |
|---|---|
| Nozzle temperature | 250 – 270 °C |
| Build surface material | Any surface |
| Build surface treatment | PVA glue or MAGIGOO PC |
| Build plate temperature | 90 - 105 °C |
| Cooling fan | OFF |
| Printing speed | 30-50 mm/s |
| Raft separation distance | 0.2 mm |
| Retraction distance | 1 mm |
| Retraction speed | 20 mm/s |
| Environmental temperature | 90-100 °C |
| Threshold overhang angle | 45 ° |
| Recommended support material | PolyDissolve™ S2 |
*All specimens were conditioned at room temperature for 24h prior to testing.
The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End-use performance of printed parts depends not only on materials, but also on part design, environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.
Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/recycling practices of Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Polymaker shall not be made liable for any damage, injury, or loss induced from the use of Polymaker materials in any application.