PolyLite PLA-CF Technical Data Sheet

Product Identification

Technical Data

• Density (ISO1183, GB/T1033): 1.29 g/cm³ at 23°C
• Melt Index (210°C, 2.16 kg): 9.2 g/10min
• Glass Transition Temperature (DSC, 10°C/min): 61.8 °C
• Melting Temperature (DSC, 10°C/min): 162.4 °C
• Vicat Softening Temperature (ISO 306, GB/T 1633): 64.1 °C
• Heat Deflection Temperature (ISO 75): 1.8MPa 50.4 °C, 0.45MPa 54.0 °C
• Young’s Modulus (X-Y): 2945 ± 100 MPa
• Young’s Modulus (Z): 2143 ± 91 MPa
• Tensile Strength (X-Y): 28.28 ± 0.7 MPa
• Tensile Strength (Z): 12.54 ± 0.7 MPa
• Elongation at Break (X-Y): 4.2 ± 0.12 %
• Elongation at Break (Z): 0.75 ± 0.08 %
• Bending Modulus (X-Y): 3215 ± 182 MPa
• Bending Strength (X-Y): 54.2 ± 1.4 MPa
• Charpy Impact Strength (X-Y): 4.82 ± 0.14 kJ/m²

Printing Parameters

• Nozzle Temperature: 190 – 220 (℃)
• Build Surface Material: BuildTak®, Glass, Blue Tape
• Build Surface Treatment: Glue
• Build Plate Temperature: 30 - 60 (˚C)
• Cooling Fan: ON
• Printing Speed: 30-70 (mm/s)
• Retraction Distance: 3 (mm)
• Retraction Speed: 40 (mm/s)

Note

The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End-use performance of printed parts depends not only on materials, but also on part design, environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.

Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/recycling practices of Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Polymaker shall not be made liable for any damage, injury or loss induced from the use of Polymaker materials in any application.


Click here to shop PolyLite PLA-CF.