Technical Data Sheet
Product Identification
| Product Name |
PolyLite LW-PLA |
| Product Use |
3D Printing Filament |
| Manufacturer/Supplier |
JF Polymers (Suzhou) Co., Ltd. |
| Address |
2901 Auburn Rd, Auburn Hills, MI 48326 |
| Contact Email |
info@rev1tech.com |
| Telephone |
+248-707-2950 |
| Emergency Telephone Number |
+248-707-2950 |
Description
PolyLite™ LW-PLA is enabled by foaming technology. It has a low density to print lightweight parts (0.6g/cm3) and features a very matte surface finish that hides layers.
Physical Properties
| Property |
Test Method |
Value |
| Density |
ISO1183, GB/T1033 |
0.8 g/cm3 at 23°C |
| Equilibrium water absorption |
- |
0.40% |
Thermal Properties
| Property |
Test Method |
Value |
| Glass transition temperature |
DSC, 10°C/min |
62.4 °C |
| Melting temperature |
DSC, 10°C/min |
150.8 °C |
| Crystallization temperature |
DSC, 10°C/min |
115.5 °C |
| Vicat softening temperature |
ISO 306, GB/T 1633 |
60.3 °C |
| Heat deflection temperature |
ISO 75 1.8MPa |
54.1 °C |
| Heat deflection temperature |
ISO 75 0.45MPa |
56.2 °C |
Mechanical Properties
| Property |
Test Method |
Value |
| Young’s modulus (X-Y) |
ISO 527, GB/T 1040 |
2636 ± 330 MPa |
| Tensile strength (X-Y) |
ISO 527, GB/T 1040 |
23.2 ± 0.4 MPa |
| Elongation at break (X-Y) |
ISO 527, GB/T 1040 |
8.21 ± 0.87 % |
| Bending modulus (X-Y) |
ISO 178, GB/T 9341 |
2607 ± 50 MPa |
| Bending strength (X-Y) |
ISO 178, GB/T 9341 |
52.9 ± 0.3 MPa |
| Charpy impact strength (X-Y) |
ISO 179, GB/T 1043 |
2.06 ± 0.19 kJ/m2 |
Printing Guidelines
- Nozzle temperature: 190 – 210°C
- Build surface material: BuildTak®, Glass, Blue Tape
- Build surface treatment: Glue
- Build plate temperature: 25 - 60°C
- Cooling fan: ON
- Printing speed: 30-50 mm/s
- Raft separation distance: 0.2 mm
- Retraction distance: 3 mm
- Retraction speed: 40 mm/s
- Environmental temperature: Room temperature - 45°C
- Threshold overhang angle: 45°
- Recommended support material: PolySupport™ and PolyDissolve™ S1
Notes
The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End-use performance of printed parts depends not only on materials but also on part design, environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.
Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/recycling practices of Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Polymaker shall not be made liable for any damage, injury, or loss induced from the use of Polymaker materials in any application.